PARAMETER

Unit

SPECIFICATION

TEST METHOD

Melt Index

g/10min

≤0.5

ASTM D1238

Density

g/cm3

0.945~0.978

ASTM D1505

Tensile Strength

MPa

≥20.0

ASTM D638

Elonggation at Break

%

≥650

ASTM D638

Brittle Temperature at Low Temperature

°C

≤-76

ASTM D746

ESCR, FO

h

≥500

ASTM D1693

Oxidation Induction Period at 200 °C

Min

≥30

ASTM D3895

Content of Carbon Black

%

2.60±0.25

ASTM D1603

Carbon Black dispersion

--

≥6

GB2951

Absorption Coefficient

--

≥400

Veka Softening Point

°C

≥110

ASTM D1525

Dielectric Strength

MV/m

≥25

ASTM D149

Volume Resisitivity

Ω.m

≥1×1014

ASTM D257

Dielectric Constant

--

≤2.75

ASTM D150